Belzona 1812 Ceramic Carbide FP 2kg Kit Epoxy Resin Based Repair Composite Bonding for Metal Pipe Valve Room Temperature Cure Particle Abrasion Protection Solvent Free Two Component Base + Solidifier

Belzona 1812 Ceramic Carbide FP 2kg one Kit Two-component Base 1.639kg + Solidifier 0.361kg = 2kg A 2-part epoxy-based composite material combining extremely hard closely packed abrasion resistant ceramic aggregates in a polymeric binder for the repair and protection of equipment damaged by fine particle abrasion. Developed for situations involving fine particle erosion such as cement manufacture. This new generation technology creates a smoother but highly durable composite capable of being applied in thin layers, providing greater opportunities to modify profiles and improve flow. Key Benefits Feature: High abrasion and wear resistance Will not corrode Solvent-free allowing it to be applied safely in confined areas Excellent bonding to many metal surfaces including steel and cast iron Application and cure at room temperature - no hot work involved Long working life Fast cure rate ensures prompt return to service High mechanical strength Applications Function: Protection of pipework, pipe bends, elbows and valves from damage due to abrasive attack Bonding and grouting tiles and wear plates where high abrasion resistance is required Repair of screw conveyors, centrifuges and pump impellers damaged by erosion and corrosion Linings for worn hoppers, chutes, mixer blades and other equipment subject to abrasion Application Temperature: 41 °F to 86 °F (5 °C to 30 °C). Working Life: The usable life of mixed material will typically be 20 minutes at 77 °F (25 °C). Volume Capacity: 29.62 in³/kg (485.4 cm³/kg). Base Color: Grey Solidifier Color: Red Mixing Ratio by Weight (Base: Solidifier): 4.5:1 Mixing Ratio by Volume (Base: Solidifier): 4.0:1 Mixed Density: 2.06 g/cm³

• Belzona 1812 Ceramic Carbide FP. 2kg one Kit. Two-component Base 1.639kg + Solidifier 0.361kg = 2kg. A 2-part epoxy-based composite material combining extremely hard closely packed abrasion resistant ceramic aggregates in a polymeric binder for the repair and protection of equipment damaged by fine particle abrasion.
• The application should ideally occur from 41 °F to 86 °F (5 °C to 30 °C). Volume Capacity: 29.62 in³/kg (485.4 cm³/kg). Mixing Ratio (Base: Solidifier) by Weight: 4.5:1; by Volume: 4.0:1. Mixed Density: 2.06 g/cm³. Base Color: Grey, Solidifier Color: Red. Touch-Dry Time: At 70 °F (22 °C) 4½ hours; At 50 °F (10 °C) 8 hours. Slump Resistance: Nil at 0.5 in. (12.7 mm).
• Developed for situations involving fine particle erosion such as cement manufacture. Protects pipes, bends, elbows, valves from abrasion. Bonds tiles and wear plates needing high abrasion resistance. Repairs screw conveyors, centrifuges, pump impellers damaged by erosion. Lines worn hoppers, chutes, mixer blades, abrasion-prone equipment.
• High abrasion and wear resistance. Corrosion-resistant. Solvent-free, safe for confined areas. Bonds well to metals like steel, cast iron. Room temperature application, no hot work needed. Long working life. Fast cure for quick service return. High mechanical strength.
• Curing Time Table (0.24in. / 6mm Thickness): Movement or use with no loading 16hrs/41°F(5°C), 8hrs/50°F(10°C), 6hrs/59°F(15°C), 4hrs/68°F(20°C), 3hrs/77°F(25°C), 2hrs/86°F(30°C); Machining or light loading 24hrs/41°F(5°C), 12hrs/50°F(10°C), 9hrs/59°F(15°C), 6hrs/68°F(20°C), 4hrs/77°F(25°C), 3hrs/86°F(30°C); Full mechanical or thermal loading 7days/41°F(5°C), 5days/50°F(10°C), 4days/59°F(15°C), 3days/68°F(20°C), 2days/77°F(25°C), 1.5days/86°F(30°C)